| APPARENT SPECIFIC DENSITY | 2727 Kg/m3 |
| OPEN POROSITY COEFFICIENT | 0,07% |
| WATER ABSORPTION COEFFICIENT | 0,04% |
| COMPRESSIVE STRENGTH-DRY CONDITION | 70,26 N/mm2 (716,65 kg/cm2) |
| COMPRESSIVE STRENGTH-WET CONDITION | 57,76 N/mm2 (589,5 kg/cm2) |
| FLEXURAL STRENGTH-DRY CONDITION | 29,97 MPa (305,69 kg/cm2) |
| RESISTANCE TO TENSION FROM BENDING-WET CONDITION | 21,25 MPa (216,75 kg/cm2) |
| FLEXURAL STRENGTH | 31,35 GPa |
| ABRASION RESISTANCE/ BOEHME | 2,04 mm |
| IMPACT STRENGTH | 60 cm |
| RESISTANCE TO TENSION FROM BENDING AFTER TEMPERATURE CHANGES (20 CYCLES) | 26,25 MPa (267,75 kg/cm2) |
| TENSION RESISTANCE FROM BENDING AFTER FROST DEFROST | 20,59 MPa (210 kg/cm2) |